Žgan aluminijev oksid in ognjevzdržni materiali

Sufficient fine grinding of the α-Al2O3 aggregates can destroy their aggregated state and make them non-porous primary crystals, at which time the particle size means close to its grain size. Activated alumina is calcined alumina that has been sufficiently finely ground and has α-Al2O3 with an original crystal size of less than 1 μm as the basic composition (20% to >90 odstotkov ). Pri proizvodnji aktiviranega aluminijevega oksida je običajno potrebno močno mletje, kot je suho mletje v s keramično obloženim krogličnim mlinom s keramičnimi kroglami kot mletjem več kot 24 ur. Razlog, zakaj se imenuje aktivirani aluminijev oksid, običajno pomeni, da je pri sintranju enostavno doseči najvišjo gostoto sintranja, vendar je temperatura sintranja 100-200 stopinj nižja kot pri nizkoaktivnem prahu -Al2O3; Enostavno reagira in sintra z drugimi komponentami v matrici materiala, kot je združevanje z glino v matrici, da se tvori mulit, reakcija s kalcijevim aluminatnim cementom, da se tvori CA6, reakcija z MgO, da se tvori spinel, itd. V skladu s teorijo sintranja , velikost zrn močno vpliva na hitrost sintranja v začetni fazi, to je na nastanek in rast vratu med zrni. Če velikost zrn zmanjšamo na 1/10 prvotne velikosti (npr. s 5 μm na 0,5 μm), bo sintranje 1000-krat do 10000-krat lažje. To pojasnjuje visoko toplotno aktivnost aktiviranega aluminijevega oksida.

Postopek mletja porabi veliko energije, zato bolj droben je prah, dražji je. Pojav silicijevega mikro (meglenega SiO2, ki nastane med proizvodnjo silicijevega karbida ali silicijeve kovine) je močno prispeval k razvoju ulitkov z nizko vsebnostjo vlage, nizko vsebnostjo cementa in ultra nizko vsebnostjo cementa, vendar ta aktivni SiO2 tudi omejuje ulitke. Delovna temperatura. Če ni uspešnega razvoja aktiviranega aluminijevega oksida, se sodobna industrija ognjevarnih materialov ne more razvijati tako hitro in delovna temperatura ne bo presegla 1600 stopinj.

 Generally speaking, powders can be divided into two categories according to the shape of particle size distribution (PSD for short): one type has a unimodal PSD, that is, the particle size distribution curve only surrounds a special particle size (close to but not necessarily Yes D50) peak: the other type is the PSD with multi-peak, that is, there are two or more distribution peaks on the PSD curve. Whether it is unimodal or bimodal, generally the wider the PSD range, the greater the powder bulk density or green body density. The PSD powder with unimodal and narrow range has the lowest bulk density. Of course, activated alumina also has the above two types. The unimodal activated alumina is characterized by a higher percentage (>80 odstotkov ) delcev<1μm (≈primary="" crystal="" size),="" and="" thus="" has="" a="" higher="" activity,="" and="" the="" average="" value="" of="" their="" particle="" size="" (≈grain="" size)="" is="" 0.30.="" around="" 5μm.="" the="" density="" of="" this="" activated="" alumina="" green="" body="" is="" low,="" usually="" only="" 54%="" 55%="" of="" the="" theoretical="" density="" of="" α-al2o3="" (3.98g/cm3),="" but="" its="" density="" after="" firing="" at="" 15001600="" ℃="" can="" reach="" 98%="" of="" the="" theoretical="" density,="" or="" even="" higher.="" unimodal="" activated="" alumina="" is="" easily="" and="" completely="" dispersed="" in="" water="" with="" the="" aid="" of="" dispersants="" such="" as="" sodium="" polyphosphate.="" the="" content="" of="" active="" particles="" smaller="" than="" 1="" μm="" in="" the="" multi-bee="" activated="" alumina="" varies="" greatly.="" usually="" between="" 20%="" and="" 7o%.="" the="" ratio="" of="" the="" number="" of="" active="" particles="" to="" the="" number="" of="" larger="" particles="" (="">1 μm) določa njegovo sposobnost in aktivnost polnjenja praznin. Za multimodalno aktivirani aluminijev oksid lahko srednji premer D50 predstavlja le njegovo finost in ne parameter, ki označuje njegove lastnosti. Zelena gostota multimodalnega aktiviranega aluminijevega oksida lahko običajno doseže 62 odstotkov 68 odstotkov teoretične vrednosti, kar je očitno višje od gostote unimodalno aktiviranega aluminijevega oksida. Sintrana gostota, ki jo lahko doseže multimodalni aktivirani aluminijev oksid, je odvisna od njegove aktivnosti. Ko se multimodalni aluminijev oksid z večjo aktivnostjo uporablja za stiskanje in sintranje, čeprav je njegova temperatura sintranja 100-150 stopinj višja od temperature popolnoma zgoščenega unimodalno aktiviranega aluminijevega oksida, je njegova sintrana gostota samo 94 odstotkov in 96 odstotkov teoretične vrednosti. Delci se zlahka ločijo od večjih delcev, zato je multimodalno aktiviran aluminijev oksid enostavno dispergirati v vodi. Širok razpon PSD multimodalnega aktiviranega aluminijevega oksida omogoča, da se mikroprah -Al2O3 zapolni v reže med agregati ognjevzdržnih zidakov in ulitkov ter v preostale praznine med velikimi delci prahu. Zato se lahko pri uporabi v ulitkih za doseganje enake tekočnosti količino dodane vode zmanjša za 4 odstotke in 5 odstotkov. V matrici litja multimodalni aktivirani aluminijev oksid deluje kot mazivo med velikimi delci, kar lahko zmanjša rahljanje litja, tudi če je izpostavljen intenzivnemu mešanju ali črpanju. hranite ločeno drug od drugega.